电工钢硅钢片 DW470-50 0.5*1200实力雄厚

电工钢硅钢片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example:

电工钢硅钢片：本文件的符号和相应的说明见表1。表 1 符号和说明符号 单位 说明P W/kg 比总损耗，通常称为铁损P1.5/50 W/kg 磁极化强度在1.5T、河南周口附近频率在50Hz下测得的比总损耗P1 W/kg 横向试样的比总损耗值P1.5/50 P2 W/kg 纵向试样的比总损耗值P1.5/50 T1.5/50 ％ 比总损耗P1.5/50的各向异性H A/m 磁场强度J T 磁极化强度J1000 T 磁场强度峰值为1000A/m下测得的磁极化强度峰值J2500 T 磁场强度峰值为2500A/m下测得的磁极化强度峰值J5000 T 磁场强度峰值为5000A/m下测得的磁极化强度峰值J10000 T 磁场强度峰值为10000A/m下测得的磁极化强度峰值μ0 H/m 真空中的磁导率取4?×10-7 B T 磁感应强度，B＝μ0H＋JReL MPa 下屈服强度Rm MPa 抗拉强度A ％ 断后伸长率C Ω·cm2/面或Ω·mm2/面 表面绝缘电阻系数RA Ω·cm2/片或Ω·mm2/片 层间电阻系数